Heat Cured Coating

HEAT CURED COATINGS

SÄKAPHEN® HEAT-CURED COATINGS OFFER HIGH-END CORROSION PROTECTION AGAINST ALL SORTS OF AGGRESSIVE MEDIUMS. SÄKAPHEN® GUARANTEES EXCELLENT PROTECTION AGAINST STRONGLY ACIDIC AND STRONGLY ALKALINE MEDIUMS, ESPECIALLY AT HIGH TEMPERATURES. SÄKAPHEN® HEAT CURED COATINGS ARE ONLY APPLIED BY SÄKAPHEN® IN GLADBECK, GERMANY AND BY ITS INTERNATIONAL LICENSEES.

SÄKAPHEN® heat-cured coatings offer excellent protection against aggressive alkaline and acidic chemicals. This applies for the gas phase as well as the immersion phase. SÄKAPHEN® heat-cured coatings are based on phenolic and phenolic epoxy resins combinations. They are hydrophobic and resistant to water vapour diffusion. SÄKAPHEN® heat-cured coatings offer an extremely high chemical resistance at temperatures above 120°C and are not susceptible to extreme temperature fluctuations. SÄKAPHEN® heat-cured coatings prevent incrustation and fouling and thus reduce investment and maintenance costs. Heat-cured coatings are applied in workshops.

SAEKAPHEN HAS A RANGE FOR DIFFERENT APPLICATIONS SI 14 EG/ 14 E /57E/57EG/57E –HC/17 E

Please visit www. Saekaphen.de

SAEKAPHEN Si 14 E

Phenolic based, hydrophobic heat-cured coating for strongly acidic to slightly alkaline media. Green, high gloss.

SÄKAPHEN® Si 14 E is a high-quality, hydrophobic phenolic based duroplastic heat-cured coating. The coating is chemically resistant to organic and inorganic acids, salt solutions, aliphatic and aromatic hydrocarbons, fume gases, alcohols, cooling water including brackish, river and sea water as well as deionized water. The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

For the coating of heat exchangers, air coolers, condensers,  turbines and compressor rotors, impellers, salt dissolving installations, pipeworks, prover loops, centrifuges, tank containers.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SAEKAPHEN Coating Si 14 E - Product Data Sheet

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Dark Green
Surface Glossy
pH Range pH 1 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180-200
Coverage at 1000µm approx. kg/m²/DFT 1 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no time limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 213
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 20
Salt spray test hours 1400
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 0,89
Surface tension mN/m > 28 < 35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 2,65

SAEKAPHEN Si 14 EG

PHENOLIC BASED HEAT-CURED COATING RESISTANT AGAINST WATER VAPOUR DIFFUSION FOR WEAK ACIDIC TO SLIGHTLY ALKALINE MEDIA. RED, MATT.

SÄKAPHEN® Si 14 EG is a high quality phenolic based heat-cured duroplastic coating, resistant to water vapor diffusion (ΔT 85 °C). The coating is chemically resistant to various weak acidic to light alkaline aqueous liquids and vapors, fume gases, organic and inorganic acids, aromatic and aliphatic solvents, all types of cooling waters including brackish, river and sea water. The surface is hard elastic.

Fields of application:

For the coating of condensers, condensate receivers, evaporators, thermal degassers, hot water and steam stressed plant parts, uninsulated tanks. Especially suitable for plant parts that are exposed to hot water and steam in neutral and acidic environment. The coating is resistant to water vapour diffusion.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 14 EG - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Iron oxide red
Surface Matt
pH Range pH 3 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 250
Coverage at 1000µm approx. kg/m²/DFT 1,3 kg / m² / 250µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 134
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 20
Salt spray test hours under examination
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 2,00
Surface tension mN/m n/a
Abrasion resistance mg/1000 r. under examination
Crosscut class 1
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 3,46

SAEKAPHEN Si 17 E

PHENOLIC BASED, HYDROPHOBIC, ELECTRICALLY CONDUCTIVE HEAT-CURED COATING FOR STRONGLY ACIDIC TO SLIGHTLY ALKALINE MEDIA. OFFERS EXCELLENT ABRASION AND IMPACT RESISTANCE. OLIVE, SATIN FINISH.

SÄKAPHEN® Si 17 E is a high-quality, hydrophobic, electrically conductive  phenolic based duroplastic heat-cured coating, resistant to water vapor diffusion (ΔT 85 °C). The coating is chemically resistant to various liquid and gaseous aliphatic and aromatic hydrocarbons, organicand inorganic acids, salt solutions, oils and greases, acidic to weak alkaline liquids up to max.pH 8. SÄKAPHEN® Si 17 E  also provides high impact resistance and abrasion resistance. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

Suitable for the coating of steel containers for storage and transportation of inflammable liquids classified as dangerous according to class AI / AII and B as well as for water endangering flammable liquids (aliphatic and aromatic chlorinated hydrocarbons) due to an electrical volume resistance below 107Ω.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

Salt spray test: Pdf download here

SÄKAPHEN® Coating Si 17 E - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Olive
Surface Satin finished
pH Range pH 2 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,2 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 9 V
Pendulum hardness acc. to König 6° sec 134
Shore D Hardness Shore D 95
Adhesion Test N/mm² [MPa] >30
Salt spray test hours 1250
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 2,8
Surface tension mN/m >38 <41
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 9,24

SAEKAPHEN Si 57 E

PHENOLIC EPOXY BASED, HYDROPHOBIC HEAT-CURED COATING FOR SLIGHTLY ACIDIC TO STRONGLY ALKALINE MEDIA. BROWN, HIGH GLOSS.

SÄKAPHEN® Si 17 E is a high-quality, hydrophobic, electrically conductive  phenolic based duroplastic heat-cured coating, resistant to water vapor diffusion (ΔT 85 °C). The coating is chemically resistant to various liquid and gaseous aliphatic and aromatic hydrocarbons, organicand inorganic acids, salt solutions, oils and greases, acidic to weak alkaline liquids up to max.pH 8. SÄKAPHEN® Si 17 E  also provides high impact resistance and abrasion resistance. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

Suitable for the coating of steel containers for storage and transportation of inflammable liquids classified as dangerous according to class AI / AII and B as well as for water endangering flammable liquids (aliphatic and aromatic chlorinated hydrocarbons) due to an electrical volume resistance below 107Ω.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

Salt spray test: Pdf download here

SÄKAPHEN® Coating Si 17 E - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Olive
Surface Satin finished
pH Range pH 2 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,2 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 9 V
Pendulum hardness acc. to König 6° sec 134
Shore D Hardness Shore D 95
Adhesion Test N/mm² [MPa] >30
Salt spray test hours 1250
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 2,8
Surface tension mN/m >38 <41
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 9,24

SAEKAPHEN Si 57 E-HC black

PHENOLIC EPOXY BASED, HYDROPHOBIC HEAT-CURED COATING FOR SLIGHTLY ACIDIC TO STRONGLY ALKALINE MEDIA WITH DOUBLE HEAT TRANSFER RATE. BLACK, GLOSS.

SÄKAPHEN® Si 57 E-HC is a high-quality, hydrophobic phenolic epoxy based heat cured duro plastic coating with double heat transfer rate. The coating is chemically resistant to strong alkaline to weak acidic substances, all type of cooling waters including brackish, river and sea water as well as deionized water, salt solutions, greases, oils, solvents, gases. The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

In particular for the coating of heat exchangers and air coolers where increased thermal conductivity is required.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 57 E-HC - Product Data


Properties Heat Cured Duroplast Coating
Resin base Phenolic epoxy resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Black
Surface Glossy
pH Range pH 3 – 14
wet coating thickness in 1 layer µm 70
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,0 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec n/a
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 30
Salt spray test hours n/a
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,29
Surface tension mN/m >28 < 35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 5,10

SAEKAPHEN Si 57 EG

PHENOLIC EPOXY BASED, HYDROPHOBIC HEAT-CURED COATING FOR SLIGHTLY ACIDIC TO STRONGLY ALKALINE MEDIA WITH DOUBLE HEAT TRANSFER RATE. BLACK, GLOSS.

SÄKAPHEN® Si 57 E-HC is a high-quality, hydrophobic phenolic epoxy based heat cured duroplastic coating with double heat transfer rate. The coating is chemically resistant to strong alkaline to weak acidic substances, all type of cooling waters including brackish, river and sea water as well as deionized water, salt solutions, greases, oils, solvents, gases. The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

In particular for the coating of heat exchangers and air coolers where increased thermal conductivity is required.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 57 E-HC - Product Data

Properties Heat Cured Duroplast Coating
Resin base Phenolic epoxy resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Black
Surface Glossy
pH Range pH 3 – 14
wet coating thickness in 1 layer µm 70
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,0 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec n/a
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 30
Salt spray test hours n/a
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,29
Surface tension mN/m >28 < 35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 5,10

SÄKAPHEN® SI 570 AR

PHENOLIC EPOXY BASED, HYDROPHOBIC COATING FOR STRONGLY ALKALINE TO LIGHT ACID MEDIA. OFFERS EXCELLENT ABRASION RESISTANCE. DARK GREY, SATIN FINISH.

SÄKAPHEN® Si 570 AR is a high-quality, hydrophobic, phenolic epoxy based heat-cured duroplastic coating. The coating is chemically resistant to liquids, fumes and mist (also in droplets) of strong alkaline to weak acidic media, all types of cooling waters including brackish, river and sea water as well as deionized water, salt solutions, greases, oils, solvents, gases. SÄKAPHEN® Si 570 AR offers excellent abrasion resistance especially for rotating equipment. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

In particular for the coating of impellers and parts that are exposed to aggressive and abrasive alkaline substances at high temperature.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 570 AR - Product Data

Properties Heat Cured Duroplast Coating
Resin base Phenolic epoxy resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Dark grey
Surface Satin finished
pH Range pH 4-13
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,8 kg / m² / 250µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 132
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 30
Salt spray test hours n/a
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,94
Surface tension mN/m <28
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK n/a

SÄKAPHEN® SI 57 EL

PHENOLIC EPOXY BASED, HYDROPHOBIC HEAT-CURED COATING FOR SLIGHTLY ACIDIC TO STRONGLY ALKALINE MEDIA FOR THE COATING OF FINNED AIR COOLERS. DARK BROWN, HIGH GLOSS.

SÄKAPHEN® Si 57 EL is a high quality, hydrophobic phenolic epoxy based heat cured duroplastic coatingoptimized for the coating of finned air coolers, especially with a small fin pitch. The coating is chemically esistant to fumes and mist also in droplets of strong alkaline to weak acidic media, all type of cooling waters including brackish, river and sea water as well as deionized water, salt solutions, greases, oils, solvents, gases. The surface is hard-elastic with hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

Optimized for the application on finned air coolers. Due a particular low viscosity finned air coolers with a fin pitch from 1,5mm upwards can be protected.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 57 EL - Product Data

Properties Heat Cured Duroplast Coating
Resin base Phenolic epoxy resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Dark Brown
Surface Glossy
pH Range pH 3 – 14
wet coating thickness in 1 layer µm 50
Total dry film thickness µm 30
Coverage at 1000µm approx. kg/m²/DFT 0,4 kg / m² / 60µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 200
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] >30
Salt spray test hours 1400
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,12
Surface tension mN/m <28
Abrasion resistance mg/1000 r. not relevant
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK 2,51

SÄKAPHEN® SI 35 E

PHENOLIC EPOXY BASED, HYDROPHOBIC COATING FOR ACIDIC TO ALKALINE MEDIA IN CONTINOUSLY CHANGING CONDITION. OFFERS EXCELLENT ABRASION AND IMPACT RESISTANCE AS WELL AS DIFFUSION RESISTANCE. GREY, SATIN FINISH

SÄKAPHEN® Si 35 E is a high-quality, hydrophobic, phenolic epoxy based heat-cured duroplastic coating resistant to water vapor diffusion (ΔT 85 °C). The coating is chemically resistant to various substances ranging from acidic to alkaline liquids and vapors, aromatic and aliphatichydrocarbons, all types of cooling waters including brackish, river and sea water as well as deionized water, oils and greases in continously changing conditions. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

Coating to be used in high temperature environment were 2 component materials will fail to ensure resistance to acidic as well as alkaline substances in operational conditions that may change on a continuing basis. Resistant to water vapour diffusion.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 35 E - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic epoxy resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Grey / olive
Surface Satin finished
pH Range pH 1-13
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,1 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 103
Shore D Hardness Shore D 92
Adhesion Test N/mm² [MPa] >20
Salt spray test hours n/a
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 3,00
Surface tension mN/m >48 <56
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK n/a

SÄKAPHEN® SI 17 TC ANTIBACTERIAL

PHENOLIC BASED, HYDROPHOBIC COATING FOR ACIDIC TO SLIGHTLY ALKALINE MEDIA. OFFERS EXCELLENT ABRASION AND IMPACT RESISTANCE AS WELL AS DIFFUSION RESISTANCE. REDDISH, SATIN FINISH.

SÄKAPHEN® Si 17 TC Antibacterial is a high-quality, abrasion and impact resistant, hydrophobic phenolic based duroplastic heat-cured coating, resistant to water vapor diffusion (ΔT 85 °C). The coating has active germicidal properties. The coating is chemically resistant to various mediums ranging from strongly acidic to light alkaline aqueous liquids and vapors, fume gases, organic and inorganic acids, chlorinated aromatic and alphatic hydrocarbon, all types of cooling waters including brackish, river and sea water as well as deionized water, oils and greases. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

For the coating of ISO tank containers, process vessels, pipe works, rotating equipment and other equipment where excellent chemical resistance as well as abrasion resistance and/or diffusion resistance is needed in combination with antibacterial properties of the coating.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 17 TC Antibacterial - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color reddish
Surface Satin finished
pH Range pH 2 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,1 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C (depending on medium)
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 153
Shore D Hardness Shore D 95
Adhesion Test N/mm² [MPa] >30
Salt spray test hours 1250
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,27
Surface tension mN/m >38 <41
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK n/a

SÄKAPHEN® SI 17 TC

PHENOLIC BASED, HYDROPHOBIC COATING FOR ACIDIC TO SLIGHTLY ALKALINE MEDIA. OFFERS EXCELLENT ABRASION AND IMPACT RESISTANCE AS WELL AS DIFFUSION RESISTANCE. ANTHRACITE, SATIN FINISH.

SÄKAPHEN® Si 17 TC is a high-quality, abrasion and impact resistant, hydrophobic phenolic based duroplastic heat-cured coating, resistant to water vapor diffusion (ΔT 85 °C). The coating is chemically resistant to various mediums ranging from strongly acidic to light alkaline aqueous liquids and vapors, fume gases, organic and inorganic acids, chlorinated aromatic and alphatichydrocarbon, all types of cooling waters including brackish, river and sea water as well as deionized water, oils and greases. The surface has hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

For the coating of ISO tank containers, process vessels, pipe works, rotating equipment and other equipment where excellent chemical resistance as well as abrasion resistance and/or diffusion resistance is needed.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

Salt spray test: Pdf download here

SÄKAPHEN® Coating Si 17 TC Antibacterial - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Anthracite
Surface Satin finished
pH Range pH 2 – 8
wet coating thickness in 1 layer µm 100
Total dry film thickness µm 180
Coverage at 1000µm approx. kg/m²/DFT 1,1 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 85°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 153
Shore D Hardness Shore D 95
Adhesion Test N/mm² [MPa] >30
Salt spray test hours 1250
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 1,27
Surface tension mN/m >38 <41
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK n/a

SÄKAPHEN® SI 14 E BKW

PHENOLIC BASED, HYDROPHOBIC HEAT-CURED COATING AS TOP COAT FOR SI 14 E FOR STRONGLY ACIDIC TO SLIGHTLY ALKALINE MEDIA, ESPECIALLY FOR CHLORINATED HYDROCARBONS. GREEN, HIGH GLOSS.

SÄKAPHEN® Si 14 E BKW is a high quality, hydrophobic phenolic based duroplastic heat-cured coating as top coat for Si 14 E. The coating is chemically resistant to organic and inorganic acids, salt solutions, aliphatic and aromatic chlorinated hydrocarbons. The surface is hard elastic with hydrophobic properties and prevents caking, fouling and incrustation.

Fields of application:

Filler-free and pigment-free top coat for Si 14 E, especially for the use inside tank containers, vessels and containers carrying chlorinated hydrocarbons.

(The images are for illustration purposes only and may differ from the actual appearance of the products.)

SÄKAPHEN® Coating Si 57 E-HC - Product Data

Properties Heat Cured Duroplast
Resin base Phenolic resin blend
Cure Mechanism Heat cured
Quantity of components 1
Color Klar
Surface Glossy
pH Range pH 1 – 8
wet coating thickness in 1 layer µm 50
Total dry film thickness µm 25-30
Coverage at 1000µm approx. kg/m²/DFT 0,2 kg / m² / 200µm
Surface Preparation Sa SA2 ½ – SA 3
Surface Profile µm 40 – 60 µm
Temperature resistance dry (dry air oven) °C -20°C to +180°C/200°C
Temperature resistance wet (water) °C -20°C to +180°C/200°C
Resistance to water vapor diffusion °C ≤ ∆T 30°C
Overcoating Waiting Time hours/23°C no limitations
Chemical Curing days after final bake
Linear Thermal Expansion µm n/a
Pore testing Volts 67,5
Pendulum hardness acc. to König 6° sec 214
Shore D Hardness Shore D 94
Adhesion Test N/mm² [MPa] > 20
Salt spray test hours under examination
Impact Strength mm (1 kg) > 1000
Surface smoothness (Ra) µm Ø 3 readings 0,53
Surface tension mN/m > 28 < 35
Abrasion resistance mg/1000 r. under examination
Crosscut class 0
Heat conductivity Ø 12,7×2,0mm on C-Steel with 67,37 w/mK W/mK n/a